探究有机玻璃表层材质的前景

Study of organic glass surface material prospects

作者:  来源:http://www.jrpmma.com/  日期:2014/5/6 12:09:12
Author:  Source:http://www.jrpmma.com/  DateTime:2014/5/6 12:09:12

常用的有机溶剂有乙醇、异丙醇、丙醇、丁醇等。加入有机溶剂的目的是为了使反应产物分散均匀,在涂覆时有机玻璃耐磨涂层研究进展易于流平,并对有机玻璃表面产生一定的溶蚀作用,有利于提高附着力。水解催化剂一般为酸性催化剂,如稀盐酸、稀硝酸等,也可以采用有机酸如醋酸等。缩合催化剂一般为碱性物质,如苛性钾、苛性钠、乙酸钠等,也有报道采用乙酸胆碱。

聚硅氧烷类涂料常用的助剂主要有2类:一类是为了进一步提高耐磨性,如胶体二氧化硅、胶体氧化锑等,以胶体二氧化硅最为常用,一般固含量在30%以下,胶体粒径在200nm以下;另一类是为了提高涂层的防紫外线能力,品种有胶体二氧化钛、胶体氧化铈等,以胶体二氧化钛最为常用。有时将二者共同使用,可使涂层的强度和防紫外线性能都得到提高。但由于这两种助剂固化后形成无机网络结构,与有机玻璃的附着力不如有机硅氧烷,因此一般不宜加入太多。如果希望增大无机网络结构所占的比例,一般需要对基材进行底涂处理。此外,为了增强涂料的其它功能,如可着色性、抗静电性等,还可加入季铵盐类物质,如三乙基烯丙基溴化铵。

由于紫外线装置廉价易得,因此多采用紫外线固化方式,使用光敏引发剂来引发自由基聚合。常用的光敏引发剂有安息香醚类、二苯酮类,一般加入比例为聚合物含量的1% 5%.由于单体聚合时容易受空气中氧的影响而发生阻聚现象,因此最好在氮气或其它惰性气氛中进行。

为进一步提高多官能团丙烯酸酯涂料的耐磨性,可在该类涂料1中引入聚硅氧烷或胶体二氧化硅结构,一般采用含有乙烯基团的有机硅氧烷水解缩聚或与胶体二氧化硅共水解缩聚的产物。由于有机硅氧烷中的乙烯基团可与丙烯酸酯官能团发生共聚,因此形成涂料的均匀性和成膜性较好,形成的涂层硬度也有所提高。

结语通过近半个世纪的发展,有机玻璃耐磨涂层在美国、日本及欧洲发达国家已获得广泛的应用,聚硅氧烷和多官能团丙烯酸酯两条路线已经成熟并相互结合向复合功能化方向发展,如耐磨兼顾导电、减反射及防紫外线、防静电等。同时新的路线、新的工艺也在不断发展,聚氨酯涂料因其独有的柔韧性将在该领域占有一席之地,等离子体化学气相沉积镀层技术作为新的工艺路线,可以将多种功能的涂层组合,发展空间广阔,但要实现大尺寸不规则成型件的涂覆均匀性,降低成本,还有许多困难需要克服。

Common organic solvents ethanol, isopropanol, n-propanol, n-butanol etc..The addition of organic solvent to the reaction product evenly dispersed in the coating, research progress on PMMA abrasion resistant coating is easy to flow, and has certain / solution 0 Effect on organic glass surface, is beneficial to improve the adhesion. Hydrolysis catalyst for acid catalystssuch as hydrochloric acid, nitric acid, etc., can also be used in organic acids such as acetic acid etc.. Condensation catalyst usually alkaline substances,such as caustic soda, caustic soda, sodium acetate, have reported usingacetic acid choline.

Polysiloxane coatings commonly used additives mainly has 2 kinds: one kind is to further improve the wear resistance, such as colloidal silica,colloidal antimony oxide, with colloidal silica is most commonly used, generalsolid content below 30%, colloid diameter below 200nm; the other is toimprove the anti ultraviolet ability of coating, varieties colloidal TiO2,colloidal ceria, using colloidal TiO2 is most commonly used. Sometimes will use the common two, can make the coating strength and anti ultravioletperformance have been improved. But because these two kinds of additivesand solidified to form inorganic network structure, and the adhesion assiloxane organic glass, so in general should not add too much. If you want to increase the proportion of inorganic network structure, the general need for substrate coating process. In addition, in order to enhance the otherfunctional coatings, such as colorability, antistatic etc, also can join thequaternary ammonium compounds, such as three ethyl allyl bromide.

The ultraviolet ray device is cheap, so the ultraviolet curing method, using photosensitive initiator to initiate free radical polymerization. Commonly used photoinitiator benzoin ethers, two phenyl ketones, adding ratio ofpolymer content 1% 5%. as the monomer polymerization is easily affected by the oxygen in air and polymerization phenomenon, so the best innitrogen or other inert atmosphere.

To improve the wear resistance of the polyfunctional acrylate coatings, thesilicone or colloidal silica structure into the coating in the product 1, thehydrolysis and condensation of siloxane containing vinyl group or with colloidal silica hydrolysis and condensation. The vinyl group silicone in Mayand copolymerization of acrylate functionality, thus forming a coatinguniformity and film is good, hardness of the coating formation is increased.

Conclusion through nearly half a century of development, organic glasscoating have been widely used in America, Japan and European countries,polysiloxane and multifunctional acrylate two routes have been mature andcombined with each other to composite functional direction, such as wearand Gu conductive, anti reflection and anti UV, anti-static. At the same timethe new route, the new technology unceasingly is also developing,polyurethane coatings because of its unique flexibility will occupy a space for one person in the field, plasma chemical vapor deposition coatingtechnology as a new technology, the coating may be a combination of various functions, a broad space for development, but to achieve the large size and irregular shaped parts evenly coated sex, reduce costs, and many difficulties to be overcome.